1.Product Description
RX-101AB-N3 is a modified epoxy resin adhesive, mixed with moderate viscosity, fast curing speed, good workmanship;
The main advantage of the cured metal ,ABS, fiber and other materials, good adhesion, good toughness, good weathering performance; applicable to carbon fiber hand-pasted products such as: sports equipment, automotive modification parts and other products of the bottom surface of the brush and cloak.
2.Technical Data
| Performance |
RX-101A-N3 |
RX-101B-N3 |
| Color |
Black viscous liquid |
Light yellow transparent liquid |
| Stickiness 40ºC/cps |
900±100 |
900±150 |
| Proportion g/cm³ |
1.15-1.20 |
1.10-1.15 |
| Shelf life 25ºC |
6 Months |
6 Months |
| Mixing ratios |
A:B=1: 1(Weight Ratio) |
| Mixing viscosity 40ºC/cps |
900±100 |
| Availability time |
25ºC/15-25 Minutes (Mixing Volume 100 g) |
| Curing conditions (1) |
60ºC/1 hour or room temperature 3.5-5 hours basic curing |
Curing conditions: These conditions are for reference only, please determine the curing conditions according to the specific needs of the product.
3.Properties after curing
| Items |
Unit |
Value |
| Durometer |
Shore D |
>=65 |
| Compressive Strengths |
kg/cm² |
6.6 |
| Impact Strength |
kg/cm² |
5.8 |
| Tensile strength, 23±2ºC, 2 days |
MPa |
≥23 |
| Steel to steel tensile shear strength, 23±2°C, 2 days |
MPa |
≥13 |
| Carbon fiber bond strength to iron, 23±2°C, 2 days |
MPa |
≥18 |
| Water absorption 25ºC |
% |
<=0.15 |
| Non-volatile matter content |
% |
≥99.3 |
| Elongation, 23±2ºC, 7 days |
% |
3.0±0.5 |
4.Precautions
1. Use the glue strictly according to the weight ratio and mix it completely;
2. When the relative humidity is greater than 85%, the surface of the cured material is easy to absorb the water in the air, the formation of matte, therefore, when the relative humidity is greater than 85%, it is recommended that the curing environment to be dehumidification treatment or do not do room temperature curing, and the use of curing temperature;
3. The higher the operating temperature, the shorter the available time and the faster the curing speed; the lower the operating temperature, the longer the available time and the slower the curing;
4. Please close the lid tightly after use to avoid quality problems caused by moisture intrusion.
This product is a high-performance epoxy fiber adhesive that can be used for effective penetration bonding between substrates such as concrete, steel, ceramics, stone, wood components, and fiber fabrics such as carbon fiber, glass fiber, aramid fiber, etc.
5.Shipping information
Restrictions
This product is not classed as dangerous goods for transport and can be shipped to all destinations without restriction.
Package Size
There are no package size restrictions or surcharges for this product.
){kind=link}
){kind=link}